Polymaker PolyWood
This Specialty family provides unique filaments from Polymaker to unlock new 3D printing applications.
Polymaker PolyWood is a wood mimic filament without actual wood powder, which removes all risks of nozzle clogs. PolyWood is made entirely with PLA using a special foaming technology. It exhibits the same density and appearance as wood.
Print Settings
Nozzle Temperature:
190˚C – 210˚C
Printing Speed:
30mm/s – 50mm/s
Bed Temperature:
25˚C – 60˚C
Bed Surface:
Glass with glue, blue tape, Buildtak
Cooling Fan:
ON
Based on 0.4 mm nozzle and Simplify 3D v.3.1. Printing conditions may vary with different printers and nozzle diameters
Mechanical Properties
Young’s Modulus:
2636 ± 330 Mpa
Tensile Strength:
23.2 ± 0.4 Mpa
Bending Strength:
52.9 ± 0.3 Mpa
Shore Hardness:
2.1 ± 0.2 kJ/m2
Thermal Properties
Glass Transition Temperature:
62˚C
Vicat Softening Temperature:
60˚C
Melting Temperature:
151°C
Notes
Drying Settings:
55˚C for 6h
Recommended Support Materials:
PolyDissolve S1
Other:
N/A
Print Settings
Polymaker PolyWood features Polymaker’s Jam-Free™ technology and Polymaker’s Stabilized Foaming™ technology:
Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams.
Stabilized Foaming™ technology is used to produce foamed filaments, whose foam structure can survive the printing process and be inherited by the printed parts. This enables light weight 3D printed parts with unprecedented surface finish.