This filament is made of polyamide 12 reinforced with 15 % of milled carbon fibers. It is characterized by high strength, high thermal and chemical resistance, great processing stability, and rheological properties. The material is suitable for the production of continually stressed parts, such as bearings, cogwheels, reinforcement parts, etc.
Features:
Always use gluestick (Elmer's, Deli得力, or Magigoo recommended by Fillamentum) for ideal bed adhesion! Because of great adhesion to other materials, plastics, composites, and glass, it can damage your bed without adhesive.
Moisture sensitive, dry 3-4 hours before use and keep in a protective sachet. If the stringing occurs, re-dry the filament.
Hot Chamber/enclosure recommended.
You might also like
Product Description:
The nylon filaments provide great chemical and wear resistance. The objects are printed with high inter-layer adhesion. The functionality of objects is good under a wide range of temperatures.
Nylon CF15 Carbon is made of polyamide 12 reinforced with 15 % of milled carbon fibers. It is characterized by high strength, high thermal and chemical resistance, great processing stability, and rheological properties. The material is suitable for the production of continually stressed parts, such as bearings, cogwheels, reinforcement parts, etc.
 |
| Material Type | Nylon CF15 Carbon (15% Carbon Fibre reinforced) |
| Tolerance | ± 0.1 mm |
| Print Temperature | 235°C-260°C |
| Melt Flow Index | 9.92g/10 min |
| Part Cooling Fan | 0% (Turn off cooling) |
| Heated Bed Temperature | 80°C-110°C |
| Heated Bed Surface | PEI, mirror/ glass |
| Adhersive | Glue stick, PVA glue |
| Raft / Skirt / Brim | Brim > 10 mm / raft |
| Heated Chamber / Enclosure | Recommended |
| Print Speed | 20 - 50 mm/s |
| Net Weight | 600g per Spool |
| Material Density | 1.08 g/cm3 |
| Tensile Strength | 54.5 MPa |
| Elongation at break | 103% |
| Charpy Impact Strength | 86.2kJ/m² |
| Tensile Modulus | 500 MPa |
| Hardness | 75 Shore D |
| Melting Temperature | Good |
| Drying Time | 3-4 hours |
| Drying Temperature | 80 °C |
| Need To Dry | High Importance |
| Moisture Affects | Stringing, Mechanical Properties get worse |